离子液体体系卤水提锂的洗涤工艺研究

溶剂萃取法是盐湖提锂的重要工艺方法。采用磷酸三丁酯（TBP）/1-丁基-3-甲基咪唑双三氟甲基磺酰亚胺盐（[C₄mim][NTf₂]）离子液体体系对高镁锂比盐湖卤水中的锂进行萃取分离提取实验,对负载有机相的洗涤和反萃过程进行了研究。萃取实验：在TBP与[C₄mim][NTf₂]体积比为9∶1、相比（有机相与水相的体积比）为2∶1条件下,锂离子与其他离子的分离系数分别为β（锂/钠）=94.70、β（锂/钾）=148.85、β（锂/镁）=131.81。洗涤实验：系统考察了洗涤剂种类及浓度、相比、洗涤次数等因素对杂质离子洗脱率的影响,结果发现氯化锂和盐酸的混合溶液是从负载有机相中洗涤除去杂质离子的有效洗涤剂。洗涤过程适宜条件：洗涤剂中氯化锂浓度为4 mol/L、盐酸浓度为0.5 mol/L,相比为5∶1,洗涤次数为2次。反萃实验：用稀盐酸（1.0 mol/L）对负载有机相进行反萃取,在相比为1∶1条件下,单级反萃率达到97.81%。研究表明,离子液体体系作为一种新型萃取体系,在高镁锂比盐湖卤水中提取锂具有较好的应用前景。     

Strain‐rate‐dependent mechanical properties of polypropylene separator for lithium‐ion batteries

The mechanical integrity of battery separators is critical for battery safety and durability. A comprehensive study of strain‐rate‐dependent tensile and puncture properties of a polypropylene lithium‐ion battery separator is presented here with a new model. Due to anisotropy of the polymeric membrane, tensile testing was conducted for different directions. Results showed that tensile strength and elastic modulus were increased 1000% and 500%, respectively, for different directions. It was also demonstrated that tensile strength changed 10 to 25% with strain rate (1.67 × 10^?4 to 1.67 × 10^?1 s^?1) for different directions. An equation was obtained for the first time for flow stress versus strain rate at varied tensile directions with respect to machine direction. Moreover, puncture testing was performed and it was shown that puncture strength was increased 140% with increasing strain rate from 0.25 to 250 mm min^?1. Two failure modes were also observed in puncture samples. Finally, Eyring's model was used to calculate activation enthalpy of the porous polypropylene separator. © 2020 Society of Chemical Industry     

Biofortification with selenium and lithium improves nutraceutical properties of major winery grapes in the Midwestern United States

Enriching the micronutrients, selenium (Se) and lithium (Li), in grapes to improve their nutraceutical properties were implemented by foliar application of organic fertiliser rich in Se and Li onto five grape cultivars. The effects of this biofortification on vine vigour, fruit quality, overall micronutrients and phenolic compounds also were investigated. Agronomic biofortification was found greatly increased the Se and Li content in the whole grape by multiple times, meanwhile it did not significantly affect the vine vigour and fruit quality of grapes. However, the biofortification did impact the Ionome (including all the mineral nutrients and trace elements) and phenolic compounds in grapes and this varied among cultivars. This study demonstrated foliar spray of organic Se/Li fertiliser was a very effective strategy to biofortify these micronutrients in grape berries, particularly in the skin, and therefore might be a promising strategy to increase the consumption and awareness of these grapes.     

Rational Designs for Lithium-Sulfur Batteries with Low Electrolyte/Sulfur Ratio

Lithium-sulfur batteries (LSBs) are considered a promising next-generation energy storage device owing to their high theoretical energy density. However, their overall performance is limited by several critical issues such as lithium polysulfide (PS) shuttles, low sulfur utilization, and unstable Li metal anodes. Despite recent huge progress, the electrolyte/sulfur ratio (E/S) used is usually very high (≥20 µL mg⁻¹), which greatly reduces the practical energy density of devices. To push forward LSBs from the lab to the industry, considerable attention is devoted to reducing E/S while ensuring the electrochemical performance. To date, however, few reviews have comprehensively elucidated the possible strategies to achieve that purpose. In this review, recent advances in low E/S cathodes and anodes based on the issues resulting from low E/S and the corresponding solutions are summarized. These will be beneficial for a systematic understanding of the rational design ideas and research trends of low E/S LSBs. In particular, three strategies are proposed for cathodes: preventing PS formation/aggregation to avoid inadequate dissolution, designing multifunctional macroporous networks to address incomplete infiltration, and utilizing an imprison strategy to relieve the adsorption dependence on specific surface area. Finally, the challenges and future prospects for low E/S LSBs are discussed.     

Rapid synthesis of garnet-type Li7La3Zr2O12 solid electrolyte with superior electrochemical performance

Li₇La₃Zr₂O₁₂-based garnet-type solid electrolytes are promising candidates for use in all-solid-state lithium batteries (ASSLBs). However, their potential in large-scale commercial applications is largely hindered by the time/energy-consuming and lithium-wasting synthetic method which typically needs a long-duration high temperature solid state reaction process. Herein we invent a fast preparation route that involves a short-period thermal reaction (1100 °C for 10 min) in laboratory muffle furnaces following by conventional hot pressing technique to get almost fully dense (Al, Ga, Ta, Nb)-doped garnet-type electrolytes with high phase purity (>99.9 %). The large and compact grains, low porosity and high phase purities of garnet ceramic electrolytes synthesized in this study ensure superior electrochemical performance. Particularly, Ga-doped cubic Li₇La₃Zr₂O₁₂ shows extremely low E_a values (0.17?0.18 eV) and record-high lithium ionic conductivities (>2 × 10^?3 S cm^-1 at 25 °C).     

冷轧预变形对新型铝锂合金的时效析出与力学性能影响

采用大气熔炼铸造及热变形方法制备了Al-4.5Cu-1Li-0.7Mg-1Zn-0.3Ag-0.3Mn-0.2Zr新型铝锂合金板材。通过维氏硬度、拉伸性能、扫描电镜、透射电镜等方法，研究了固溶后不同冷轧预变形量对显微组织和力学性能影响。结果表明，时效前的冷轧预变形量有效促进了新型铝锂基体合金中T1(Al2CuLi)相的析出与均匀分布，减少了θ′(Al2Cu)相的体积分数。冷轧预变形量的增加，缩短了峰时效时间，晶界析出相由连续析出变为非连续析出，无沉淀析出区宽度变小。当冷轧预变形量为15%时，时效态合金的屈服强度与抗拉强度分别达到了668 MPa、690 MPa，延伸率保持在7.9%。     

Polymer electrolytes and interfaces in solid-state lithium metal batteries

The polymer electrolyte based solid-state lithium metal batteries are the promising candidate for the high-energy electrochemical energy storage with high safety and stability. Moreover, the intrinsic properties of polymer electrolytes and interface contact between electrolyte and electrodes have played critical roles for determining the comprehensive performances of solid-state lithium metal batteries. In this review, the development of polymer electrolytes with the design strategies by functional units adjustments are firstly discussed. Then the interfaces between polymer electrolyte and cathode/anode, including the interface issues, remedy strategies for stabilizing the interface contact and reducing resistances, and the in-situ polymerization method for enhancing the compatibilities and assembling the batteries with favorable performances, have been introduced. Lastly, the perspectives on developing polymer electrolytes by functional units adjustment, and improving interface contact and stability by effective strategies for solid-state lithium metal batteries have been provided.     

Novel electrospun polymer electrolytes incorporated with Keggin‐type hetero polyoxometalate fillers as solvent‐free electrolytes for lithium ion batteries

In this study, solvent‐free nanofibrous electrolytes were fabricated through an electrospinning method. Polyethylene oxide (PEO), lithium perchlorate and ethylene carbonate were used as polymer matrix, salt and plasticizer respectively in the electrolyte structures. Keggin‐type hetero polyoxometalate (Cu‐POM@Ru‐rGO, Ni‐POM@Ru‐rGO and Co‐POM@Ru‐rGO (POM, polyoxometalate; rGO, reduced graphene oxide)) nanoparticles were synthesized and inserted into the PEO‐based nanofibrous electrolytes. TEM and SEM analyses were carried out for further evaluation of the synthesized filler structures and the electrospun nanofibre morphologies. The fractions of free ions and crystalline phases of the as‐spun electrolytes were estimated by obtaining Fourier transform infrared and XRD spectra, respectively. The results showed a significant improvement in the ionic conductivity of the nanofibrous electrolytes by increasing filler concentrations. The highest ionic conductivity of 0.28 mS cm^?1 was obtained by the introduction of 0.49 wt% Co‐POM@Ru‐rGO into the electrospun electrolyte at ambient temperature. Compared with solution‐cast polymeric electrolytes, the electrospun electrolytes present superior ionic conductivity. Moreover, the cycle stability of the as‐spun electrolytes was clearly improved by the addition of fillers. Furthermore, the mechanical strength was enhanced with the insertion of 0.07 wt% fillers to the electrospun electrolytes. The results implied that the prepared nanofibres are good candidates as solvent‐free electrolytes for lithium ion batteries. © 2020 Society of Chemical Industry     

硫酸铵法利用中低品位锂瓷土矿制备碳酸锂技术研究

针对江西宜丰地区氧化锂质量分数<2.0%以下中低品位锂瓷土矿,研究了硫酸铵法提取碳酸锂技术路线。首先,利用二步焙烧工艺,有利于脱氟、提高锂浸出率,并且能够有效防止结窑现象发生。在浸出液除杂过程中,采用成矾除铝的方法将大量溶出的铝离子转变为KAl（SO₄）₂·12H₂O、NH₄Al（SO₄）₂·12H₂O等有价值复盐,规避了传统石膏法产生的大量固废,有70%的铝离子被转变为矾盐晶体,同时带出大量的结晶水,减轻后续浓缩压力,对比传统的石膏法产生大量固废而言,其优点是显而易见的。碳化反应产品的XRD以及氧化锂含量分析表明,碳酸锂的纯度达到99%以上,全程锂收率为50%~60%。作为提锂实验对比,采用宜春414矿锂质量分数为4.0%的锂云母,由于414矿样中铝的相对含量更低,导致相同的除杂难度下得到的414矿样中浸出液锂离子浓度更高,浓缩倍数更小,414矿样的锂回收率更高。实验结果表明,中低品位锂瓷土提锂的工艺规律,通过适当改变参数,能够应用于难度更低的高品位的锂云母提锂过程。     

Synthesis of highly efficient,structurally improved Li4SiO4 sorbents for high-temperature CO2 capture

Li₄SiO₄ sorbents for high-temperature CO₂ removal have drawn extensive attention owing to their potential application in carbon capture and storage (CCS). The major challenge in the application lies in the poor CO₂ capture performance under realistic conditions of low CO₂ concentrations, owing to the dense structure and poor porosity. In this work, Li₄SiO₄ sorbents were prepared with porous micromorphologies and large contact areas using a variety of organometallic Li-precursors, achieving fast CO₂ sorption kinetics, high capacity and excellent cyclic stability at a low CO₂ concentration (15?vol%). It was found that a high conversion of ~?74% was maintained for pure Li₄SiO₄ even after 100 sorption/desorption cycles. Moreover, by doping with Na₂CO₃ to reduce the CO₂ diffusion resistance, the conversion of the sorbent was further enhanced to 93.2%. The enhancement mechanism of alkali carbonate have been proven here to be ascribed to the formation of the eutectic melt of Li/Na carbonates, the existence and function of which has been confirmed in this study.